The coating of a NiTi alloy has a greater impact on the mechanical properties than the acidity of saliva
Materiali in tehnologije, 52 (2018), 4; 469-473. https://doi.org/10.17222/mit.2017.133
Pop Acev, Darko; Katić, Višnja; Turco, Gianluca; Contardo, Luca; Špalj, Stjepan

Citirajte ovaj rad

Pop Acev, D., Katić, V., Turco, G., Contardo, L. i Špalj, S. (2018). The coating of a NiTi alloy has a greater impact on the mechanical properties than the acidity of saliva. Materiali in tehnologije, 52. (4), 469-473. doi: 10.17222/mit.2017.133

Pop Acev, Darko, et al. "The coating of a NiTi alloy has a greater impact on the mechanical properties than the acidity of saliva." Materiali in tehnologije, vol. 52, br. 4, 2018, str. 469-473. https://doi.org/10.17222/mit.2017.133

Pop Acev, Darko, Višnja Katić, Gianluca Turco, Luca Contardo i Stjepan Špalj. "The coating of a NiTi alloy has a greater impact on the mechanical properties than the acidity of saliva." Materiali in tehnologije 52, br. 4 (2018): 469-473. https://doi.org/10.17222/mit.2017.133

Pop Acev, D., et al. (2018) 'The coating of a NiTi alloy has a greater impact on the mechanical properties than the acidity of saliva', Materiali in tehnologije, 52(4), str. 469-473. doi: 10.17222/mit.2017.133

Pop Acev D, Katić V, Turco G, Contardo L, Špalj S. The coating of a NiTi alloy has a greater impact on the mechanical properties than the acidity of saliva. Materiali in tehnologije [Internet]. 2018. [pristupljeno 21.10.2024.];52(4):469-473. doi: 10.17222/mit.2017.133

D. Pop Acev, V. Katić, G. Turco, L. Contardo i S. Špalj, "The coating of a NiTi alloy has a greater impact on the mechanical properties than the acidity of saliva", Materiali in tehnologije, vol. 52, br. 4, str. 469-473, 2018. [Online]. Dostupno na: https://urn.nsk.hr/urn:nbn:hr:184:588999. [Citirano: 21.10.2024.]

Za citiranje koristite ovu mrežnu adresu: https://urn.nsk.hr/urn:nbn:hr:184:588999
Prijavite se u repozitorij kako biste mogli spremiti objekt u svoju listu.
Podaci o radu
Naslov (engleski)The coating of a NiTi alloy has a greater impact on the mechanical properties than the acidity of saliva
AutorDarko Pop Acev
AutorVišnja Katić
AutorGianluca Turco
AutorLuca Contardo
AutorStjepan Špalj
Autorova ustanovaSveučilište u Rijeci
Medicinski fakultet
(Katedra za ortodonciju)
Znanstveno / umjetničko
područje, polje i grana		BIOMEDICINA I ZDRAVSTVO
Dentalna medicina
Sažetak (engleski)
The aim of this study was to evaluate the influence of the acidity of saliva on changes to the surface roughness, friction and microhardness of NiTi alloys with various coatings. Three types of commercially available NiTi archwires: uncoated, rhodium coated and nitrified (dimension 0.508×0.508 mm, 10 cm long) were immersed in 10 mL of artificial saliva with the pH ranging from 4.8 to 6.6 for a period of 28 d. Surface roughness, friction and microhardness were analyzed and compared to the unexposed as-received wires. These mechanical properties were influenced by the wire coating with a moderate-to-high effect size (p<=0.005 ; n2=0.132-0.309). The uncoated wire had a lower maximum roughness depth after exposure to pH 6.6 and 5.5 than the unexposed wire (p=0.026 ; n2=0.346). The friction was significantly increased only in the rhodium- coated NiTi at pH 4.8 compared to the lower acidities and the unexposed wire (p=0.005 ; n2 =0.437). No correlation was found between pH, surface roughness, friction and microhardness, respectively. The coating of a NiTi alloy has a greater impact on the mechanical properties than the acidity does. A rhodium coating makes the alloy harder, induces a rougher surface and more friction. Nitrification does not alter the alloy as much. The relation between acidity and mechanical properties is not linear. A high acidity of 4.8 induces a high friction, but only in rhodium-coated NiTi. A lower acidity does not change the friction significantly.
Ključne riječi (engleski)
Jezikengleski
Vrsta publikacijeZnanstveni rad - Izvorni znanstveni rad
Status objaveObjavljen
Vrsta recenzijeRecenziran
Verzija publikacijeObjavljena verzija rada (izdavačev PDF)
Naslov časopisaMateriali in tehnologije
Brojčani podacivol. 52, br. 4, str. 469-473
p-ISSN1580-2949
DOIhttps://doi.org/10.17222/mit.2017.133
URN:NBNurn:nbn:hr:184:588999
Datum objave publikacije2018
URL dokumentahttp://bib.irb.hr/950780
Vrsta resursaTekst
Prava pristupaOtvoreni pristup
Uvjeti korištenjaIkona licence Imenovanje-Nekomercijalno-Bez prerada 4.0 međunarodna (CC BY-NC-ND 4.0)
Datum i vrijeme pohrane2022-03-10 10:42:51